Integrated circuit devices having features with reduced edge curvature and methods for manufacturing the same

ABSTRACT

A structure such as an integrated circuit device is described having a line of material with critical dimensions which vary within a distribution substantially less than that of a mask element, such as a patterned resist element, used in manufacturing the line of material.

BACKGROUND

1. Field of the Invention

The present invention relates to integrated circuit fabrication, and more particularly to methods for fabricating high-density integrated circuit devices.

2. Description of Related Art

Photolithographic processes can be used to form a variety of integrated circuit structures on a semiconductor wafer. In photolithography, features of these structures are typically created by exposing a mask pattern (or reticle) to project an image onto a wafer that is coated with light sensitive material such as photo resist. After exposure, the pattern formed in the photo resist may then be transferred to an underlying layer (e.g. metal, polysilicon, etc.) through etching to create the desired features.

One problem associated with manufacturing devices having very small features arises because of variations introduced by the photolithographic processes. Specifically, resist material properties, process conditions, optical distortions and other factors can cause systematic and random deviations in the etched shapes of the features from their desired shapes. Examples of deviations include corner-rounding, line-shortening and line edge roughness.

In a typical lithographic patterning process, a line of resist is used as an etch mask to create a corresponding line of material in the underlying layer. In such a case, the deviations in the patterned line of resist will be transferred to the critical dimensions of the line in the underlying layer. As process technologies continue to shrink, these deviations become a greater percentage of the critical dimension of the line of material, which can reduce yield and result in significant performance variability in devices such as transistors implemented utilizing these lines of material.

Accordingly, it is desirable to provide high-density structures such as integrated circuit devices which overcome or alleviate issues caused by deviations introduced by photolithographic processes, thereby improving performance and manufacturing yield of such devices.

SUMMARY

A structure such as an integrated circuit device is described having a line of material with critical dimensions which vary within a distribution substantially less than that of a mask element, such as a patterned resist element, used in manufacturing the line of material. An amorphization and partial recrystallization process is described for defining a sidewall surface of the line of material, which does not carry the sidewall surface variations of the mask element introduced by photolithographic processes, or other patterning processes, involved in forming the mask element. The mask element is used as an ion implantation mask to form an amorphous phase region within the layer of crystalline phase material. The partial recrystallization process straightens the amorphous/crystalline material interface through crystalline growth at energetically favorable step or kink sites of the interface. The remaining portion of the amorphous phase region is then selectively removed to leave the sidewall surface of the line of material. As a result of this process, the variation of the sidewall surface of the line of material can be controlled much tighter than the variation in the sidewall surface of the mask element. This results in the line of material having improved line definition, with straighter edges and sharper corners, than is possible using the mask element as an etch mask. In embodiments of the technology described herein, the line edge roughness of the line of material is less than or equal to 1 nm, which is much less than is possible utilizing lithographic etch mask technologies.

A method for manufacturing a structure as described herein includes forming a mask element, such as a patterned resist element, overlying a layer of crystalline phase material such as a semiconductor substrate. Ions are implanted into the layer using the mask element as an implantation mask, thereby converting a region of the layer into an amorphous phase. The amorphous phase region has a first interface with crystalline phase material underlying the mask element. The amorphous phase region is then partially recrystallized to form a recrystallized portion adjacent the first interface and leave a remaining portion in the amorphous phase. The remaining portion has a second interface with the recrystallized portion. The remaining portion of the amorphous phase region is then selectively removed to leave a sidewall surface in the layer at a location defined by the second interface.

A structure as described herein includes a line of crystalline phase material having a first sidewall surface and a second sidewall surface. The first sidewall surface and the second sidewall surface each have a line edge roughness less than or equal to 1 nm. In embodiments described herein, the line of crystalline phase material further has a line width roughness between the first sidewall surface and the second sidewall surface that is less than or equal to 1.5 nm.

The above summary of the invention is provided in order to provide a basic understanding of some aspects of the invention. This summary is not intended to identify key or critical elements of the invention or to delineate the scope of the invention. Its sole purpose is to present some concepts of the invention in a simplified form as a prelude to the more detailed description that is presented later. Other aspects and advantages of the present invention can be seen on review of the drawings, the detailed description, and the claims which follow.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-4 illustrate stages in a manufacturing process flow of an embodiment of the amorphization and partial recrystallization process described herein.

FIGS. 5A-5F illustrate an example of the partial recrystallization process for straightening out the amorphous/crystalline material interface through crystalline growth at energetically favorable step or kink sites of the interface.

FIGS. 6A-6C illustrate an example simulation of the partial recrystallization process.

FIG. 7 illustrates an example simulation of the partial recrystallization process for various surfaces along different planes of a crystal lattice of a material having a diamond cubic crystal structure.

FIGS. 8-11 illustrate stages in a manufacturing process flow of the amorphization and partial recrystallization process illustrated in FIGS. 2-4, using the mask element illustrated in FIG. 8.

FIGS. 12-14 illustrate stages in a manufacturing process flow of a second embodiment of the amorphization and partial recrystallization process described herein.

DETAILED DESCRIPTION

The following description is presented to enable any person skilled in the art to make and use the invention, and is provided in the context of a particular application and its requirements. Various modifications to the disclosed embodiment will be readily apparent to those skilled in the art, and the general principles defined herein may be applied to other embodiments and applications without departing from the spirit and scope of the present invention. Thus, the present invention is not intended to be limited to the embodiments shown, but is to be accorded with the widest scope consistent with the principles and features disclosed herein.

FIGS. 1-4 illustrate stages in a manufacturing process flow of an embodiment of the amorphization and partial recrystallization process described herein. It will be understood that the process steps and structures described with reference to FIGS. 1-4 do not describe a complete process for the manufacturing of an integrated circuit device. The amorphization and partial recrystallization process described herein can be utilized in the manufacturing of various types of integrated circuit components.

FIGS. 1A and 1B (collectively “FIG. 1”) illustrate top and cross-sectional views respectively of a mask element 100 patterned on a material layer 110. The mask element 100 has a first sidewall surface 102 and a second sidewall surface 104. The mask element 100 may be formed by patterning a layer of photoresist using a lithographic process. For example, the mask element 100 may be formed for example using 193 nm lithography, extreme ultraviolet (EUV) radiation, electron beams, nanoimprint lithography, spacer lithography, or double patterning. Alternatively, other materials and patterning processes may be used to form the mask element 100.

The material layer 110 is a layer of crystalline phase material. As described in more detail below, the material layer 110 is a material which can be selectively etched when in an amorphous phase, relative to the crystalline phase of the material. The material layer 110 may for example comprise silicon or other semiconductor material. Alternatively, the material layer 110 may comprise other materials. In some embodiments, the material layer 110 may be an intermediate layer between an underlying layer and the mask element 100.

The mask element 100 has variations in shape as a result of imperfections and pattern fidelity limitations in the patterning process and other factors during the formation of the mask element 100. The dashed lines 101, 103 in the top view of FIG. 1A represent an idealized shape of the mask element 100. The term “line edge roughness” (LER) refers to a statistical measure, such as the standard deviation, of the actual positions of a sidewall surface relative to the mean sidewall surface position along the length of a segment of the sidewall surface. The values of LER described herein refer to a three-sigma standard deviation of the roughness of the sidewall surface, unless indicated otherwise. The term “line width roughness” (LWR) refers to a statistical measure, such as the standard deviation, of the actual line width relative to the mean line width along the length of a segment of a line having two sidewall surfaces. The values of LWR described herein refer to a three-sigma standard deviation of the roughness of the width, unless indicated otherwise.

As can be seen in FIGS. 1A and 1B, the first sidewall surface 102 and the second sidewall surface 104 each have a pronounced LER. Accordingly, the mask element 100 has a pronounced LWR.

Next, ion implantation is performed on the structure illustrated FIGS. 1A and 1B using the mask element 100 as an implantation mask, resulting in the structure illustrated in the top and cross-sectional views of FIGS. 2A and 2B (collectively “FIG. 2”). The ion implantation converts a first region 200 of the material layer 110 proximate the first sidewall surface 102 into an amorphous phase. The first region 200 has an interface 202 with crystalline phase material in a region 150 of the material layer 110 underlying the mask element 100. As shown in FIGS. 2A and 2B, the variation in the first sidewall surface 102 is carried through to the crystalline/amorphous interface 202 of the first region 200. Due to lateral scattering of the atoms, the first region 200 extends a distance beneath the mask element 100.

In the illustrated embodiment, the ion implantation is performed to amorphize the material layer 110 using a neutral species such as silicon, germanium, or xenon, so that additional charges are not introduced into the material layer 110. In some embodiments, the ion implantation is performed using atoms which are same as that of the material layer 110. For example, in one embodiment in which the material layer 110 is silicon, silicon atoms are used in the ion implantation.

The ion implantation also converts a second region 210 of the material layer 110 proximate the second sidewall surface 104 into the amorphous phase. The second region 210 has an interface 212 with the crystalline phase material in the region 150. As shown in FIGS. 2A and 2B, the variation in the second sidewall surface 104 is carried through to the crystalline/amorphous interface 212 of the second region 210.

Next, annealing is performed on the structure illustrated in FIGS. 2A and 2B to partially recrystallize the first region 200 and the second region 210, resulting in the structure illustrated in the top and cross-sectional view of FIGS. 3A and 3B (collectively “FIG. 3”). The temperature and duration of the annealing process can be determined empirically, and can vary from embodiment to embodiment.

As described in more detail below with respect to FIGS. 5A-5F, 6A-6C and 7, the partial recrystallization process straightens a crystalline/amorphous material interface along a direction parallel to a plane of the crystal lattice of the material layer 110. This straightening of the amorphous/crystalline material interface occurs through crystalline growth at energetically favorable atomic step or kink sites of the interface. The straightening depends on the temperature and duration of the annealing process, as well as which plane of the crystal lattice the interface extends along.

As shown in FIGS. 3A and 3B, the partial recrystallization of the first region 200 forms a recystallized portion 300 and a recrystallized portion 305 of the first region 200, and leaves a remaining portion 310 in the amorphous phase. The remaining portion 310 in the amorphous phase has an interface 320 with the recrystallized portion 300. As a result of the partial recrystallization process, the variation in the interface 320 is much less than the variation in the original interface 202, and thus much less than the variation in the first sidewall surface 102 of the mask element 100. In other words, the interface 320 is much straighter than the first sidewall surface 102 of the mask element 100 from which the interface 320 originated.

As is also shown in FIGS. 3A and 3B, the partial recrystallization of the second region 210 forms a recrystallized portion 330 and a recrystallized portion 335 of the second region, and leaves a remaining portion 340. The remaining portion 340 in the amorphous phase has an interface 350 with the recrystallized portion 330. As a result of the partial recystallization process, the variation in the interface 350 is much less than the variation in the original interface 212, and thus much less than the variation in the second sidewall surface 104 of the mask element 100. In other words, the interface 350 is much straighter than the second sidewall surface 104 of the mask element 100 from which the interface 350 originated.

Next, etching is performed to selectively remove the remaining portion 310 of the first region 210 and remove the remaining portion 340 of the second portion 210, resulting in the structure illustrated in the top and cross-sectional view of FIGS. 4A and 4B (collectively “FIG. 4”). The etching process selectively etches the amorphous phase material of the material layer 110, relative to the crystalline phase material of the material layer 110. The etch process used depends on the material of the material layer 110, and can vary from embodiment to embodiment. In one embodiment in which the material layer 110 is silicon, the selective etching process is performed using hydrofluoric acid (HF).

As shown in FIGS. 4A and 4B, the selective removal of the remaining portion 310 leaves a sidewall surface 400 in the material layer 110 at a location defined by the interface 320. Similarly, the selective removal of the remaining portion 340 leaves a sidewall surface 410 in the material layer 110 at a location defined by the interface 350.

The sidewall surface 400 and the sidewall surface 410 define opposing sides of a line 420 of crystalline phase material in the material layer 110. The line 420 has a line width 425. The line width 425 may be for example 15 nm, or less.

As a result of the preceding amorphization and partial recrystallization processes, the variation of the sidewall surfaces 400, 410 of the line can be controlled over a distribution much less than the variation in the sidewall surfaces 102, 104 of the mask element 100. These small variations arise because the sidewall surfaces 400, 410 have variations dependent upon the variations in the recrystallization interfaces 320, 350 used to define them. The variations in the recrystallization interfaces 320, 350 are in turn determined by the straightening of the amorphous/crystalline material interface through crystalline growth at energetically favorable atomic step or kink sites, which can be readily controlled. As a result, these variations in the sidewall surfaces 400, 410, can be controlled over a distribution much less than the variations due to photolithographic processes, or other patterning processes, involved in the formation of the sidewall surfaces 102, 104 of the mask element 100. The results in the line 420 having improved line definition, with straighter sidewall surfaces 400, 410, than is possible using the mask element 100 as an etch mask. Therefore, integrated circuit elements, such as FinFET transistors, interconnect lines or other small features such as nano-wires, implemented using the line 420 will exhibit uniform performance and high yield in a way not possible in the prior art.

As an example, using a lithographic process, the LER of the first sidewall surface 102 and the second sidewall surface 104 of the mask element 100 can be greater than 4 nm. As explained above, variations in the sidewall surfaces 400, 410 of the line 420 are substantially less than that of the variations in the sidewall surfaces 102, 104. As a result, the LER of the sidewall surfaces 400, 410 much smaller, such as for example less than or equal to 1 nm. This results in the width 425 of the line 420 having a LWR substantially less than that of the mask element 100, such as for example less than or equal to 1.5 nm.

In some embodiments the sidewall surfaces 400, 410 vary by +/− the atomic step size of the material of material layer 110. In one embodiment in which the material layer 110 is silicon, the variation is the atomic step size of silicon, +/−0.3 nm.

FIGS. 5A-5F illustrate an example of a cross-sectional view of the straightening of an amorphous/crystalline material interface 500 following an ion implantation.

FIG. 5A illustrates a cross-sectional view after performing ion implantation to convert a region 500 into an amorphous phase. The amorphous phase region 500 has an interface 504, represented by a dashed line in the Figure, with atoms arranged in a crystal lattice within crystalline phase region 510. The type of crystal lattice within region 510 depends upon the material of the region 510. In one embodiment, the atoms in region 510 are silicon atoms arranged in a diamond cubic crystal structure. Materials having other types of crystal lattices structures may alternatively be used. Due to the ion implantation, the atoms (not illustrated) in the amorphous phase region 510 are arranged randomly throughout amorphous phase region 500.

As shown in FIG. 5A, the interface 504 includes kink sites which define the roughness of the interface 504. A kink site is a location along the interface 504 where two or more atoms in the crystalline phase region 510 may be bonded with a single atom from the amorphous phase region 510. For example, kink site 520 is the location where atom 522 and atom 524 may be bonded together by a single atom. The kink sites are energetically favorable sites for crystalline growth because it is more difficult to bond an atom on an already flat crystal surface. An atom which bonds to a flat surface will include several dangling bonds, which causes the total energy of the atom to be relatively high. In contrast, an atom which bonds to a kink site will have less dangling bonds than if it were to attach to a flat surface, and thus a lower total energy. As a result, during annealing, atoms within the amorphous phase region 510 will bond at these energetically favorable kink sites, which advances crystalline growth along a crystal plane of the region 510. This in turn causes the straightening of the amorphous/crystalline interface.

FIG. 5B illustrates a stage in the progression of the partial recrystallization of the amorphous phase region 500 during annealing. As shown in FIG. 5B, an atom 530 from the amorphous phase region 510 bonds to the atoms 524 and 522 in the crystalline phase region 510, thus recrystallizing at the kink site. As can be seen upon comparison of FIGS. 5A and 5B, this causes a shift in the interface 504.

FIGS. 5C, 5D, 5E and 5F illustrate further stages in the progression of the partial recrystallization of the amorphous phase region 500 during annealing. As shown in these figures, additional atoms from the amorphous phase region 510 continue to bond at available kink sites, thus causing the interface 504 to advance and straighten.

FIGS. 6A-6C illustrate a perspective view of a simulation of the straightening of an amorphous/crystalline material interface 504 following an ion implantation. The simulation can be made using a simulator such as the Sentaurus tools available from Synopsys, Inc.

FIG. 6A illustrates a perspective view after performing ion implantation to convert a region 600 of a layer of crystalline phase material into an amorphous phase. In this example, the layer of crystalline phase material is a silicon wafer with a (100) orientation. The mask edge is along a <110> crystal direction, and amorphization is performed using Ge atoms. The amorphous phase region 600 has an interface 604 with atoms arranged in a crystal lattice within the crystalline phase region 610.

FIG. 6B illustrates a stage in the progression of the partial recrystallization of the amorphous phase region 610 during annealing. As can be seen upon comparison of FIGS. 6A and 6B, the recrystallization causes the interface 604 to shift and straighten.

FIG. 6C illustrates another stage in the procession of the recrystallization of the amorphous phase region 610 during annealing. As can be seen upon comparison of FIGS. 6B and 6C, the continued recrystallization causes the interface 604 to further shift and straighten.

FIG. 7 illustrates an example simulation of the partial recrystallization process for various surfaces along different planes of a crystal lattice for a material having a diamond cubic crystal structure. In this example, the material is silicon.

As can be seen in FIG. 7, the roughness of the amorphous/crystalline material interface depends upon which plane of the crystal lattice the interface extends along. Thus, in some embodiments, the mask element and the material layer are arranged such that the amorphous/crystalline material interface extends along a direction parallel to the plane of the crystal lattice of the material layer which will be the straightest following annealing.

As shown in FIG. 7, for the diamond cubic crystal structure, the {111} planes are the straightest after annealing, the {110} planes are the next straightest, and the {100} planes are the least straight. This variation in the straightness among the various planes occurs because a surface along the {111} planes has the slowest growth rate and a surface along the {100} planes has the fastest growth rate. Therefore, on a {111} plane, the probability that an atom will attach to a flat surface is lower the probability that an atom will attach to a flat surface on a {100} plane. Thus, in one embodiment in which the material layer comprises a material having a diamond cubic crystal structure, such as silicon, the top surface of the material layer is along a (110) plane, and the sidewalls are formed in the material layer extending along a direction parallel to a {111} plane of the diamond cubic crystal structure.

In the examples described above, the amorphization and partial recrystallization process was carried out to straighten the sidewall surfaces extending along the longer sides of an elongated line of material. As described below with respect to FIGS. 8-11, the techniques described herein can also be carried out to simultaneously straighten the sidewall surface along the shorter side of the elongated line of material, in order to sharpen the corners between the longer and shorter sides.

FIGS. 8-11 illustrate stages in a manufacturing process flow of the amorphization and partial recrystallization process illustrated in FIGS. 2-4, using the mask element 800 illustrated in FIG. 8.

FIGS. 8A and 8B illustrate top and cross-sectional views respectively of a mask element 800 patterned on the material layer 110 of crystalline phase material. The dashed lines 801, 803, 805 in the top view of FIG. 8A represent an idealized shape of the mask element 800. The mask element 800 has an elongated shape with a first sidewall surface 802 a second sidewall surface 804 along the longer sides, and a third sidewall surface 806 along a shorter side. The mask element 800 may be formed by patterning a layer of photoresist using a lithographic process. Alternatively, other materials and patterning processes may be used to form the mask element 800.

Next, ion implantation is performed on the structure illustrated FIGS. 8A and 8B using the mask element 800 as an implantation mask, resulting in the structure illustrated in the top and cross-sectional views of FIGS. 8A and 8B. The ion implantation converts a first region 900 of the material layer 110 proximate the first sidewall surface 802 into an amorphous phase. The first region 900 has an interface 902 with crystalline phase material in a region 950 of the material layer 110 underlying the mask element 800. As shown in FIGS. 9A and 9B, the variation in the first sidewall surface 802 is carried through to the crystalline/amorphous interface 902 of the first region 900. Due to lateral scattering of the atoms, the first region 900 extends a distance beneath the mask element 800.

The ion implantation also converts a second region 910 of the material layer 110 proximate the second sidewall surface 804 into the amorphous phase. The second region 910 has an interface 912 with the crystalline phase material in the region 950. The ion implantation also converts a third region 920 of the material layer 110 proximate the third sidewall surface 806 into the amorphous phase. The third region 920 has an interface 922 with the crystalline phase material in the region 950.

Next, annealing is performed on the structure illustrated in FIGS. 9A and 9B to partially recrystallize the first region 900, the second region 910 and the third region 920, resulting in the structure illustrated in the top and cross-sectional view of FIGS. 9A and 9B. The temperature and duration of the annealing process can be determined empirically, and can vary from embodiment to embodiment.

As described above, the partial recrystallization process straightens a crystalline/amorphous material interface along a direction parallel to a plane of the crystal lattice of the material layer 110.

As shown in FIGS. 10A and 10B, the partial recrystallization of the first region 900 forms a recystallized portion 1000 and a recystallized portion 1005 of the first region 900, and leaves a remaining portion 1010. The remaining portion 1010 in the amorphous phase has an interface 1020 with the recrystallized portion 1000. As a result of the partial recrystallization process, the variation in the interface 1020 is much less than the variation in the original interface 902, and thus much less than the variation in the first sidewall surface 802 of the mask element 800. In other words, the interface 1020 is much straighter than the first sidewall surface 802 of the mask element 800 from which the interface 1020 originated.

As is also shown in FIGS. 10A and 10B, the partial recrystallization of the second region 910 forms a recrystallized portion 1030 and a recrystallized portion 1035 of the second region 910, and leaves a remaining portion 1040. The remaining portion 1040 in the amorphous phase has an interface 1050 with the recrystallized portion 1030. As a result of the partial recystallization process, the variation in the interface 1050 is much less than the variation in the original interface 912, and thus much less than the variation in the second sidewall surface 804 of the mask element 800. In other words, the interface 1050 is much straighter than the second sidewall surface 804 of the mask element 800 from which the interface 1050 originated.

The partial recrystallization of the third region 920 forms a recrystallized portion 1060 of the third region 920, and leaves a remaining portion 1070. The remaining portion 1070 in the amorphous phase has an interface 1080 with the recrystallized portion 1060. As a result of the partial recrystallizaton process, the variation in the interface 1080 is much less than the variation in the original interface 922, and thus in turn much less that the variation in the third sidewall surface 806 of the mask element 800 from which the interface 1050 originated.

Next, etching is performed to selectively remove the remaining portion 1010 of the first region 900, remove the remaining portion 1040 of the second region 910, and remove the remaining portion 1070 of the third region 920. The resulting structure is illustrated in the top and cross-sectional views of FIGS. 11A and 11B.

As shown in FIGS. 11A and 11B, the selective removal of the remaining portion 1010 leaves a sidewall surface 1100 in the material layer 110 at a location defined by the interface 1020. Similarly, the selective removal of the remaining portion 1040 leaves a sidewall surface 1110 in the material layer 110 at a location defined by the interface 1050. Also, the selective removal of the remaining portion 1070 leaves a sidewall surface 1120 in the material layer 110 at a location defined by the interface 1080.

The sidewall surface 1100 and the sidewall surface 1110 define opposing sides of a line 1130 of crystalline phase material in the material layer 110. The sidewall surface 1120 extends between the sidewall surfaces 1100 and 1110 to define an end or termination of the line 1130. The line 1130 has a line width 1135.

The amorphization and partial recrystallization process results in the line 1130 having improved line definition, with straighter sidewall surfaces 1100, 1110, 1120 and sharper corners at the intersection of the sidewall surfaces, than is possible using the mask element 800 as an etch mask.

The corner rounding radius is the radius of a 90-degree arc of a hypothetical circle having a mean position along the intersection between generally perpendicular sides of a line. As an example, using a lithographic process, the corner rounding radius can be greater than 50 nm. Using the techniques described herein, the corner rounding radius can for example be less than 3 nm.

As described above, the roughness of the amorphous/crystalline material interface after annealing depends upon which plane of the crystal lattice the interface extends along. Thus, in preferred embodiments, the mask element 800 and the material layer 110 are arranged such that the subsequently formed sidewall surfaces 1100, 1110 respectively extend along a first direction parallel to one plane of the crystal lattice of the material layer 100, and the sidewall surface 1120 extends along a second direction parallel to another plane of the crystal lattice of the material layer 110. In one embodiment in which the material layer 110 is a material having a diamond cubic crystal structure, the sidewall surfaces 1100, 1110 extend along a direction parallel to one of a {111} plane and a {110} plane of the diamond cubic crystal structure, and the sidewall surface 1120 extends along a direction parallel to the other of the {111} plane and the {110} plane.

In the examples described above, the amorphization and partial recrystallization process was preferably carried out to form sidewall surfaces of the line of material extending along particular planes of the crystal lattice of the material layer 110 which are straightened during the process. However, in some devices, other considerations such as stress engineering, carrier mobility, and surface charges/traps may make it undesirable to implement certain integrated circuit elements using a line of material oriented along these particular planes. For example, certain integrated circuit elements may typically be formed in silicon using a {100} wafer with a <110> transistor direction.

As used herein, a wafer orientation is defined by its normal direction, and currently the {100} family of directions is standard in semiconductor fabrication. Because of crystallographic symmetry, all the specific directions in the {100} family have the same recrystallization properties. Whereas a family of wafer orientation directions is denoted herein with curly brackets, if a specific direction is referenced herein, it is enclosed in parentheses, such as (100). Most modern lithographic processes orient all transistors such that their longitudinal direction is the <110> family of crystallographic directions. As used herein, the “longitudinal” direction of a transistor is the direction parallel to current flow in the transistor, and the “transverse” direction of a transistor is the direction cross-wise to the current flow in the transistor. A family of lithographic orientation directions is denoted with angle brackets, whereas if a specific direction is referenced herein, it is enclosed in square brackets, such as [110].

As described below with respect to FIGS. 12-14, the techniques described herein can also be carried out to form a line of material that can then be used as an etch mask during the patterning of an underlying layer of material. In doing so, a line having straight edges and sharp corners can be formed in the underlying layer, without being limited to particular orientations within the underlying layer.

FIGS. 12-14 illustrate stages in a manufacturing process flow of a second embodiment of the amorphization and partial recrystallization process described herein.

FIGS. 12A and 12B illustrate top and cross-sectional views respectively of a mask element 1200 patterned on the material layer 110 of crystalline phase material. The dashed lines 1201, 1203 in the top view of FIG. 12A represent an idealized shape of the mask element 1200. The mask element 1200 has a first sidewall surface 1202 and a second sidewall surface 1204. The mask element 1200 may be formed by patterning a layer of photoresist using a lithographic process. Alternatively, other materials and patterning processes may be used to form the mask element 1200.

As shown in FIG. 12B, the material layer 110 is separated from material layer 1220 by an intermediate layer 1210. The intermediate layer 1210 protects the material layer 1220 during the amorphization and partial recrystallization process carried out the material layer 110 described below. The intermediate layer 1210 may comprise for example silicon dioxide. Alternatively, the intermediate layer 1210 may comprise other materials.

The material layer 1220 may for example comprise silicon or other semiconductor material. Alternatively, the material layer 1220 may comprise other materials. For example, the material layer 1220 may be polysilicon or a metal material. The multilayer structure illustrated in FIGS. 13A and 13B may for example be manufactured using silicon-on-insulator (SOI) techniques. Alternatively, rather than an SOI layer, other materials with strong anisotropic etching properties may be used for layer 110.

Next, the amorphization, partial recrystallization, and selective etching of amorphous phase material as described above with respect to FIGS. 2-4 are performed on the structure illustrated in FIGS. 12A and 12B. The resulting structure is illustrated in the cross-sectional and top views of FIGS. 13A and 13B.

As shown in FIGS. 13A and 13B, this process forms a line 1300 of material within the material layer 110. The line 1300 includes a first sidewall surface 1310 and a second sidewall surface 1320 at locations defined by amorphous/crystalline interfaces formed during the amorphization and partial recrystallization of the material layer 110.

The amorphization and partial recrystallization process results in the line 1300 having improved line definition, with straighter sidewall surfaces 1310, 1320, than is possible using the mask element 800 as an etch mask.

Next, an etching process is performed on the structure illustrated in FIGS. 13A and 13B using the line 1300 as etch mask, resulting in the structure illustrated in the top and cross-sectional views of FIGS. 14A and 14B.

As shown in FIGS. 14A and 14B, the etching leaves a sidewall surface 1410 in the material layer 1220 at a location defined by the sidewall surface 1310. Similarly, the etching leaves a sidewall surface 1420 in the material layer 1220 at a location defined by the sidewall surface 1320.

The sidewall surface 1410 and the sidewall surface 1420 define opposing sides of a line 1430 of material in the material layer 1220. The line 1430 has a line width 1435.

The etching process may be a two step process. In such a case, a first etch process can be performed to etch through the intermediate layer 1210 using the line 1300 as etch mask. A second etch process may then be performed using the remaining intermediate layer 1210 as an etch mask to form the line 1430 in the material layer 1220. Alternatively, the etching process may be a single etch process such as a plasma etch through the intermediate layer 1210 and into the material layer 1220.

Using the line 1300 in the material layer 110 to form the line 1430 in the material layer 1220 allows the sidewall surfaces 1310, 1320 of the line 1300 to extend along a particular plane of the crystal lattice of the material layer 110, without limiting the orientation of the sidewall surfaces 1410, 1420 of the line 1430 in the material layer 1220. In other words, the sidewall surfaces 1310, 1320 of the line 1300 may extend along a direction parallel to a particular plane of the crystal lattice of material layer 110, and the sidewall surfaces 1410, 1420 may extend along a direction parallel to a different plane of the crystal lattice of material layer 1220. This results in the line 1430 having improved line definition, while also enabling other factors such as stress effects to be taken into consideration when determining the orientation of the side sidewall surfaces 1410, 1420 of the line 1430.

Various types of integrated circuit devices, such as FinFET transistors, interconnect lines or other small features such as nano-wires, may be implemented using the line 1430. In addition, the line 1430 may be implemented as part of a mask pattern (or reticle) utilized during manufacturing of subsequent devices.

While the present invention is disclosed by reference to the preferred embodiments and examples detailed above, it is to be understood that these examples are intended in an illustrative rather than in a limiting sense. It is contemplated that modifications and combinations will readily occur to those skilled in the art, which modifications and combinations will be within the spirit of the invention and the scope of the following claims. 

What is claimed is:
 1. A method for manufacturing a structure, the method comprising: providing a first layer of crystalline phase material having crystallographic planes with differing epitaxial growth rates, the first layer being oriented such that a first one of the crystallographic planes having the slowest of the epitaxial growth rates extends vertically with respect to a top surface of the first layer of crystalline phase material; forming a mask element overlying the first layer of crystalline phase material; implanting ions into the first layer using the mask element as an implantation mask, thereby converting a region of the first layer into an amorphous phase, the amorphous phase region having a first interface with crystalline phase material underlying the mask element; partially recrystallizing the amorphous phase region into the crystalline phase to form a recrystallized portion adjacent the first interface and leave a remaining portion in the amorphous phase, the remaining portion having a second interface with the recrystallized portion; and selectively removing the remaining portion of the amorphous phase region to leave a first sidewall surface in the first layer at a location defined by the second interface, wherein the first sidewall extends parallel to the first one of the crystallographic planes having the slowest of the epitaxial growth rates.
 2. The method of claim 1, wherein the second interface is straighter than the first interface.
 3. The method of claim 2, wherein the first sidewall surface is straighter than the first interface.
 4. The method of claim 1, wherein the first interface has a first line edge roughness, and the second interface has a second line edge roughness less than the first line edge roughness.
 5. The method of claim 4, wherein the first line edge roughness is greater than 6 nm, and the second line edge roughness is less than or equal to 1 nm.
 6. The method of claim 4, wherein the first sidewall surface has a third line edge roughness less than the first line edge roughness.
 7. The method of claim 1, wherein the first layer comprises a material having a diamond cubic crystal structure.
 8. The method of claim 7, wherein the second interface extends along a direction parallel to a {111} plane of the diamond cubic crystal structure.
 9. The method of claim 1, wherein: implanting ions into the first layer further converts a second region of the first layer into the amorphous phase, the amorphous phase region having a third interface with the crystalline phase material underlying the mask element; partially recrystallizing further partially recrystallizes the second amorphous region into the crystalline phase to form a second recrystallized portion adjacent the third interface and leave a second remaining portion in the amorphous phase, the second remaining portion having a fourth interface with the second recrystallized portion; and selectively removing further selectively removes the second remaining portion to leave a second sidewall in the first layer at a location defined by the fourth interface.
 10. The method of claim 9, wherein the first sidewall and the second sidewall define opposing sides of a line of crystalline phase material.
 11. The method of claim 10 wherein the line of crystalline phase material has a line width roughness between the first sidewall and the second sidewall that is less than or equal to 1.5 nm.
 12. The method of claim 1, wherein forming the mask element comprises performing a lithographic process.
 13. The method of claim 1, further comprising etching a second layer underlying the first layer using the recrystallized portion as an etch mask, thereby forming a second sidewall surface in the second layer at a location defined by the first sidewall surface in the first layer.
 14. The method of claim 13, wherein the second layer comprises a material different than that of the first layer.
 15. The method of claim 13, wherein the first layer and the second layer each comprise material having a diamond cubic crystal structure.
 16. The method of claim 15, wherein the first sidewall surface in the first layer extends along a direction parallel to a first plane of the diamond cubic crystal structure of the first layer, and the second sidewall surface in the second layer extends along a direction parallel to a second plane of the diamond cubic crystal structure of the second layer, the second direction different from the first direction.
 17. The method of claim 7, wherein the top surface of the first layer is along a (110) plane.
 18. The method of claim 9, wherein the second sidewall is vertical.
 19. The method of claim 18, wherein the first and second sidewall surfaces are parallel to each other.
 20. The method of claim 18, wherein the first and second sidewall surfaces intersect each other perpendicularly.
 21. The method of claim 13, wherein the second layer comprises crystalline phase material having crystallographic planes with differing epitaxial growth rates, the second layer being oriented such that the crystallographic planes having the slowest of the epitaxial growth rates in the second layer do not extend vertically with respect to the top surface of the first layer.
 22. The method of claim 21, wherein the top surface of the first layer is along a (110) plane, and a top surface of the second layer is along a (100) plane.
 23. The method of claim 1, further comprising providing a second layer of crystalline phase material having crystallographic planes with differing epitaxial growth rates, the second layer underlying the first layer and being oriented such that a one of the crystallographic planes of the second layer having the slowest of the epitaxial growth rates does not extend vertically with respect to the top surface of the first layer, wherein implanting ions into the first layer further converts a second region of the first layer into the amorphous phase, the amorphous phase region having a third interface with the crystalline phase material underlying the mask element; wherein partially recrystallizing further partially recrystallizes the second amorphous region into the crystalline phase to form a second recrystallized portion adjacent the third interface and leave a second remaining portion in the amorphous phase, the second remaining portion having a fourth interface with the second recrystallized portion; and wherein selectively removing further selectively removes the second remaining portion to leave a second sidewall in the first layer at a location defined by the fourth interface, further comprising etching the second layer using the recrystallized portion as an etch mask, thereby forming third and fourth sidewall surfaces in the second layer at locations defined by respectively the first and second sidewall surfaces in the first layer.
 24. The method of claim 23, wherein the first layer and the second layer each comprise material having a diamond cubic crystal structure, wherein the top surface of the first layer is along a (110) plane, and wherein a top surface of the second layer is along a (100) plane.
 25. The method of claim 23, wherein the first and second sidewall surfaces in the first layer both extend along a direction parallel to the first plane.
 26. The method of claim 23, wherein the first sidewall surface in the first layer extends along a direction parallel to the first plane, and the second sidewall surface in the first layer intersects the first sidewall surface. 